08045803790

High Alumina Products

Acid Resistant Products

Refractory Item

Oil Drilling Bentonite

Electrical Earthing Bentonite

Foundry Bentonite

Iron Ore Pelletization Bentonite

Animal Feed Bentonite

Paper Bentonite

Agriculture Bentonite

Water Well Drilling Bentonite

Geosynthetic Clay Linear Bentonite

Horizontal Direction Drilling Bentonite

Water Treatment Bentonite

Construction Bentonite

Bricks

insulating and Castables Products

Industrial Minerals

Tiles & Blocks

Clay-Based Refractoriees

Ceramics Fiber

Basic Refractories

Pond Sealing Bentonite

Jaggery Powder

Boiler Bed Material

Industrial Boiler Bed Material

High Alumina Castables And Mortar Powder

Get a Price/Quote

MOQ : 20 MT Metric Tons

High Alumina Castables And Mortar Powder Specification

Surface Finish
Smooth

Application
Furnaces, kilns, boilers, incinerators, lining and repair

Water Absorption
6 8%

Chemical Composition
Al2O3 50-90%, SiO2, Fe2O3, CaO (varied)

Melting Point
1770C 1850C

Form
Powder

Hardness (%)
High

Density
2.8 Gram per cubic centimeter(g/cm3)

Usage & Applications
Construction, industrial furnaces, steel, cement, glass industries

Purity(%)
>85%

Product Type
Refractories

Types of Refractories
Castables, Mortar

Shape
Powder & Granular

Porosity
16 23%

Dimensional Stability
Excellent at High Temperatures

Strength
Cold Crushing Strength: 500 1100 kg/cm

Specific Gravity
2.6 2.8 g/cm

Thermal Conductivity
1.0 1.6 W/mK at 1000C

Color
Light Yellow to Off-white

Setting Time
Initial set: 3-5 hrs, Final set: 8-10 hrs

Storage Condition
Store in a cool, dry place away from moisture

Refractoriness Under Load (RUL)
>1350C

Contamination Resistance
Good resistance to alkalies and slags

Grain Size
0-5 mm (Customizable as per requirements)

Bonding Type
Hydraulic or Chemical (as per grade selected)

Cold Crushing Strength (CCS)
>50 MPa after 110C drying

Residual Expansion
<1% after heating to service temperature

Packaging
HDPE bags, 25 kg or 50 kg net

Service Temperature
Up to 1800C

Shelf Life
12 months from the date of manufacture in a dry, moisture-free condition

High Alumina Castables And Mortar Powder Trade Information

Minimum Order Quantity
20 MT Metric Tons

FOB Port
Mundra

Payment Terms
Delivery Point (DP), Letter of Credit (L/C), Western Union, Telegraphic Transfer (T/T), Days after Acceptance (DA)

Supply Ability
1000 Metric Tons Per Month

Delivery Time
7-12 Days

Sample Available
Yes

Sample Policy
Free samples are available

Main Export Market(s)
Australia, North America, South America, Eastern Europe, Western Europe, Middle East, Africa, Central America, Asia

About High Alumina Castables And Mortar Powder

High Alumina Castables And Mortar Powder

Highalumina mortar is manufactured using high purity calcined, reactive aluminapowder and green chrome oxide. The main characteristics of it are high purity,excellent strength and superior resistance to temperature. We are the leadingmanufacturer of High alumina castables and mortar as per clients needs andrequirements.

High alumina castablesare manufactured using high purity alumina cement. The main characteristics ofit are high purity, excellent strength and superior resistance to temperature.High alumina castables and mortar offered by CMS INDUSTRIES is known for itschemical and physical properties in the foreign markets.

Superior Thermal and Mechanical Performance

Our High Alumina Castables and Mortar Powder deliver robust strength and exceptional resistance to thermal shock, alkali, and slag attack. Engineered to withstand temperatures up to 1800C and with melting points between 17701850C, they provide outstanding dimensional stability and longevity in high-temperature furnaces and kilns. Their optimized grain size and controlled porosity ensure smooth application and reliable thermal performance across demanding industrial operations.

Versatile Application and Easy Handling

Customizable in both grain size and bonding type, these castables can be tailored to various industrial lining and repair jobs. The products smooth surface finish and excellent water absorption rates facilitate efficient installation and setting, with an initial set time of 35 hours and final set within 810 hours. Packaged in sturdy HDPE bags, the material remains clean, protected, and ready for immediate use on-site.

FAQs of High Alumina Castables And Mortar Powder:

Q: How should High Alumina Castables and Mortar Powder be used in industrial applications?

A: These castables and mortar powders are suitable for constructing and repairing linings in furnaces, kilns, boilers, and incinerators across steel, cement, and glass industries. They can be applied by casting or trowelling according to the specific design and thickness requirements. Proper mixing with clean water and installation as per guidelines ensures optimal performance.

Q: What is the storage process for maintaining product shelf life?

A: To maximize the 12-month shelf life, store the material in its original HDPE bags, in a cool, dry place away from direct moisture. Avoid storing the product near open sources of water or in high-humidity areas to prevent premature setting or degradation of quality.

Q: When is it appropriate to apply the material after mixing?

A: Once mixed with water, the High Alumina Castables and Mortar Powder should be applied within the initial setting time frame of 35 hours, and installation should be completed before the final set (810 hours). Delays beyond this period may impact workability and performance.

Q: Where can these castables and mortar powders be used?

A: The product is ideal for use in high-temperature, chemically aggressive environments such as steelmaking furnaces, cement rotary kilns, boilers, incinerators, and glass production units. Its versatility also makes it suitable for repair work wherever strong resistance to heat and corrosive substances is required.

Q: What benefits does using this high alumina product provide over conventional materials?

A: High Alumina Castables and Mortar Powders offer superior cold crushing strength, high refractoriness, low residual expansion, and excellent resistance to slag and alkali attack. This results in longer service life, reduced maintenance, and improved energy efficiency for industrial furnaces and other high-temperature applications.

Q: How is the products resistance to contamination by slags and alkalies ensured?

A: The high alumina content (5090%) and carefully selected additives provide excellent chemical stability. This composition allows the refractories to resist penetration and corrosion by slags, alkalies, and other aggressive agents commonly encountered in metallurgical and kiln environments.